PC MITSUBISHI THAILAND HL-8000
High liquidity level
US$ 3,592 / MT
FOB Shenzhen Port
Electrical performanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
Dielectric strength3.00mmIEC 60243-118 KV/mm
Dissipation factor100HzIEC 602506E-04
Volume resistivityIEC 600933E+16 ohms·cm
Dissipation factor1MHzIEC 602509E-03
Relative permittivity100HzIEC 602503.10
Surface resistivityIEC 600936E+15 ohms
Dielectric strength1.00mmIEC 60243-131 KV/mm
Relative permittivity1MHzIEC 602503.10
mechanical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
bending strengthISO 178100 Mpa
Tensile modulusISO 527-22400 Mpa
Tensile strainYieldISO 527-25.7 %
Nominal tensile fracture strainISO 527-285 %
tensile strengthYieldISO 527-265.0 Mpa
Bending modulusISO 1782500 Mpa
Physical propertiesTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
Shrinkage rateMD:3.20mm0.40-0.60 %
melt mass-flow rate300°C/1.2kgISO 1133140 g/10min
Shrinkage rateTD:3.20mm0.40-0.60 %
吸水率(Saturation,23°C)0.24 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 1133136 cm3/10min
thermal performanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B132 °C
Linear coefficient of thermal expansionTDISO 11359-26.6E-05 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A118 °C
impact performanceTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
Impact strength of simply supported beam without notch23°CISO 179NoBreak
flammabilityTest ConditionTest MethodMITSUBISHI THAILAND/HL-8000
UL flame retardant rating0.38mmUL 94V-2