Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC D2000P BK1A644 SABIC INNOVATIVE US
LNP™ LUBRILOY™
Electrical appliances,Plastic bag,Aerospace Applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1600 J/m |
| 23°C4 | ISO 180/1U | 100 kJ/m² | |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 51.0 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 横向 : -40°C | ISO 11359-2 | 6.7E-5 cm/cm/°C |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 89.0 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 6.7E-5 cm/cm/°C |
| Heat Deflection Temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距4，HDT | ISO 75-2/Af | 94.0 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 6.6E-5 cm/cm/°C |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 97.0 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| coefficient of friction | Dynamic | ASTM D3702 | 0.090 |
| elongation | 屈服 | ISO 527-2 | 4.3 % |
| Tensile modulus | --2 | ASTM D638 | 2550 Mpa |
| flexural modulus | -- | ASTM D790 | 2820 Mpa |
| elongation | 断裂 | ASTM D638 | 6.5 % |
| tensile strength | 屈服 | ASTM D638 | 67.0 Mpa |
| 屈服 | ISO 527-2 | 62.0 Mpa | |
| Tensile modulus | -- | ISO 527-2/1 | 2600 Mpa |
| elongation | 断裂 | ISO 527-2 | 6.7 % |
| 屈服 | ASTM D638 | 4.5 % | |
| bending strength | -- | ASTM D790 | 103 Mpa |
| Wear factor | ASTM D3702 | 6.0E+6 10^-8 mm³/N·m | |
| tensile strength | 断裂 | ASTM D638 | 60.0 Mpa |
| 断裂 | ISO 527-2 | 54.0 Mpa | |
| coefficient of friction | Static | ASTM D3702 | 0.22 |
| flexural modulus | -- | ISO 178 | 2800 Mpa |
| bending strength | -- | ISO 178 | 102 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| shrinkage rate | 横向流量 : 24小时 | ISO 294-4 | 0.57 % |
| 流动 : 24小时 | ASTM D955 | 0.50 % | |
| Melt volume flow rate | 300°C/1.2 kg | ASTM D1238 | 15.7 cm3/10min |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| shrinkage rate | 横向流动 : 24小时 | ASTM D955 | 0.60 % |
| 流量 : 24小时 | ISO 294-4 | 0.53 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/D2000P BK1A644 |
|---|---|---|---|
| drying time | 4.0 to 6.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 255 to 265 °C | ||
| Temperature at the rear of the barrel | 250 to 260 °C | ||
| Processing (melt) temperature | 255 to 290 °C | ||
| mold temperature | 40 to 65 °C | ||
| drying temperature | 80 °C | ||
| Temperature at the front of the material cylinder | 260 to 270 °C | ||
| Back pressure | 0.200 to 0.300 Mpa |