TPV Salflex 380A Salflex Polymers Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Salflex Polymers Ltd./Salflex 380A |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒 | ISO 868 | 82 |
| physical property | Test Condition | Test Method | Salflex Polymers Ltd./Salflex 380A |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 1.3 % | |
| density | ISO 1183/A | 0.960 g/cm³ |
| elastomer | Test Condition | Test Method | Salflex Polymers Ltd./Salflex 380A |
|---|---|---|---|
| tensile strength | 100%应变 | ISO 37 | 5.10 MPa |
| elongation | 断裂 | ISO 37 | 540 % |
| tensile strength | 断裂 | ISO 37 | 11.2 MPa |
| compression set | 125°C,70hr | ISO 815 | 60 % |
| tear strength | ISO 34-1 | 52 kN/m |
| aging | Test Condition | Test Method | Salflex Polymers Ltd./Salflex 380A |
|---|---|---|---|
| Tensile stress change rate | 125°C,70hr,在IRM903油中，断裂 | ISO 1817 | -47 % |
| Change rate of hardness (Shore) in the air | 邵氏A,150°C,168hr | ISO 188 | -1.0 |
| Change rate of tensile strength in air | 125°C,70hr,在IRM903油中 | ISO 1817 | -22 % |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 71 % |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -24 % |
| Tensile stress change rate | 150°C,168hr，断裂 | ISO 188 | -23 % |
| Thermal performance | Test Condition | Test Method | Salflex Polymers Ltd./Salflex 380A |
|---|---|---|---|
| brittle temperature | 类型B | ISO 812 | -60.0 °C |