PBT/ASA S 4090 G2 BK BASF GERMANY
Ultradur®
Laptop case、Shell、Engineering accessories、Laptop case、Applied in fields that re、As for the load-bearing p、Shell、Engineering accessories、Laptop case
Low warpage、Dimensional stability、Filler: Glass fiber reinf、10% filler by weight、filler、Glass fiber reinforced ma、10%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| Glass Fiber Content | 20 % |
| Basic performance | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| Water absorption rate | 0.4 % | ||
| melt mass-flow rate | ISO 1133 | 20 cm3/10min | |
| density | ISO 1183 | 1.39 g/cm³ |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 7 kJ/m² | ||
| tensile strength | ISO 527-1/-2 | 100 Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| ball-indentation hardness | ISO 2039-1 | 153 Mpa | |
| Tensile creep modulus | 1000Hr | ISO 899-1 | 3300 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 4500 Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 37 kJ/m² |
| bending strength | 23°C | ISO 178 | 119 Mpa |
| ISO 178 | 151 Mpa | ||
| Tensile modulus | ISO 527-1/-2 | 6900 Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 24 kJ/m² |
| 23 ℃ | 55 kJ/m² | ||
| elongation at break | 23°C | ISO 527-2 | 2.9 % |
| elongation | 断裂 | 2.5 % | |
| tensile strength | 23°C | ISO 527-2 | 75 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| dielectric strength | 1.50mm | IEC 60243-1 | 22 KV/mm |
| dielectric constant | 23°C | IEC 60250 | 3.40 1MHz |
| Surface Resistivity | IEC 60093 | 1E+14 Ω.cm | |
| Dissipation Factor | 23°C | IEC 60250 | 0.021 1MHz |
| dielectric constant | 23°C | IEC 60250 | 3.60 100HZ |
| Dissipation Factor | 23°C | IEC 60250 | 3.1E-03 100HZ |
| Volume resistivity | IEC 60093 | 1E+14 Ω.cm |
| Flame retardancy | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| UL flame retardant rating | Allcolor | UL -94 | HB 3.00mm |
| Allcolor | UL -94 | HB 0.71mm | |
| Allcolor | UL -94 | HB 1.50mm |
| processability | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| Melt Temperature | 250-270 °C | ||
| Temperature | 60-100 °C |
| physical property | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| Shrinkage rate | 纵向 | 0.16 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.40 % |
| melt mass-flow rate | 275℃/2.16Kg | ISO 1133 | 35 cm3/10min |
| Water absorption rate | 23°C,50RH | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/S 4090 G2 BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 223 °C | |
| thermal conductivity | DIN 52612 | 0.27 W/m/K | |
| Heat distortion temperature | 1.80MPa未退火，HDT | ISO 75-2/Af | 105 °C |
| Linear coefficient of thermal expansion | ISO 11359-1/-2 | 0.4 E-4/°C | |
| combustibility | UL 94 | HB | |
| Heat distortion temperature | 1.80 MPa，HDT | 160 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa未退火，HDT | ISO 75-2/Bf | 190 °C |