Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BKV15 LANXESS INDIA
Durethan®
Home appliance components、Automotive Applications、Electronic and electrical
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 20 kJ/m² |
| 23°C | ISO 180/1U | 25 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 40 kJ/m² |
| -30°C | ISO 179/1eU | 35 kJ/m² |
| hardness | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 190 Mpa |
| Supplementary Information | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| ISO Shortcut | ISO 1874 | PA6/66.GHR.14-060.GF15 |
| film | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| Thin film puncture strength | --7 | ISO 6603-2 | 2.00 J |
| --6 | ISO 6603-2 | 505 N | |
| --7 | ISO 6603-2 | 560 N | |
| --6 | ISO 6603-2 | 1.50 J |
| Electrical performance | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 30 KV/mm |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.70 |
| Volume resistivity | 23°C | IEC 60093 | 1E+13 ohms·cm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 4.10 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 8E-03 |
| 23°C,1MHz | IEC 60250 | 0.018 |
| Mechanical properties | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 3.0 % |
| Flexural modulus | 23°C | ISO 178/A | 5700 Mpa |
| bending strength | 3.5%Strain | ISO 178/A | -- Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 120 Mpa |
| bending strength | 23°C | ISO 178 | 185 Mpa |
| 23°C | ASTM D790 | 185 Mpa | |
| Tensile modulus | 23°C | ASTM D638 | 6310 Mpa |
| 23°C | ISO 527-2/1 | 6300 Mpa | |
| tensile strength | 断裂,23°C | ASTM D638 | 117 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 5700 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 3.0 % |
| bending strength | FlexuralStrainatFlexuralStrength5(23°C) | 4.0 % |
| flammability | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | ISO 4589-2 | 23 % | |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning Behavior | ISO 3795 | passed |
| physical property | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| Shrinkage rate | MD:280°C,3.00mm2 | ISO 2577 | 0.34 % |
| Apparent density | ISO 60 | 0.70 g/cm³ | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.6 % |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO 2577 | 0.67 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 7.8 % |
| Shrinkage rate | MD:120°C,2hr,3.00mm3 | ISO 2577 | 0.10 % |
| TD:120°C,2hr,3.00mm3 | ISO 294-4 | 0.21 % |
| Thermal performance | Test Condition | Test Method | LANXESS INDIA/BKV15 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 218 °C | |
| vicat | -- | ISO 306/B120 | 200 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 210 °C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 180 °C |
| vicat | -- | ISO 306/B50 | 200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 55.0 °C |