Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC ML-4104ZLP TEIJIN JAPAN
PANLITE®
Casters,Fitness equipment
Thermal stability,transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/ML-4104ZLP |
|---|---|---|---|
| tensile strength | 50mm/min，屈服 | ISO 527-1 | 64 Mpa |
| elongation at break | 50mm/min | ISO 527-1 | 100 % |
| tensile strength | 50mm/min，断裂 | ISO 527-1 | 72 Mpa |
| bending strength | 2mm/min | ISO 178 | 100 Mpa |
| Flexural modulus | 2mm/min | ISO 178 | 2500 Mpa |
| Impact strength of cantilever beam gap | Notched | ISO 179 | 15 kJ/m² |
| optical performance | Test Condition | Test Method | TEIJIN JAPAN/ML-4104ZLP |
|---|---|---|---|
| Pigment dispersion | 2.0mmt | In-house method | 47 % |
| transmittance | 1.5mmt | JIS K7136 | 63 % |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/ML-4104ZLP |
|---|---|---|---|
| Dissolving fingers | 300℃ | ISO 1133 | 18 cm310min |
| Shrinkage rate | MD | In-house method | 0.5-0.7 % |
| TD | In-house method | 0.5-0.7 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/ML-4104ZLP |
|---|---|---|---|
| Heat distortion temperature | TD，HDT | ISO 11359-2 | 0.7 X10-4/℃ |
| 线膨胀系数，MD，HDT | ISO 11359-2 | 0.7 X10-4/℃ | |
| 1.80MPa，HDT | ISO 75-1 | 122 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |