PA6 6LVG50H1 NC DOMO CHEM GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
Suspended wall beam without notch impact strength23°CISO 180/1U90 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU95 kJ/m²
Mechanical propertiesTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
Tensile modulusISO 527-2/115500 Mpa
tensile strength 断裂ISO 527-2/5210 Mpa
bending strengthISO 178320 Mpa
Flexural modulusISO 17814000 Mpa
Tensile strain断裂ISO 527-2/52.0 %
Electrical performanceTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
Volume resistivityIEC 600931.0E+15 ohms·cm
Surface ResistivityIEC 600931.0E+13 ohms
flammabilityTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
burning rateFMVSS 302< 100 mm/min
UL flame retardant rating0.8 mmUL 94HB
physical property Test ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
Shrinkage rate流量 : 23°C, 72小时ISO 25770.10 - 0.20 %
viscosity number96% H2SO4ISO 307125 cm³/g
Shrinkage rate横向流量 : 23°C, 72小时ISO 25770.40 - 0.60 %
Thermal performanceTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
melting temperatureISO 11357-3221 °C
Hot deformation temperature (HDT)0.45 MPa, 未退火，HDTISO 75-2/B220 °C
vicatISO 306/B50215 °C
Hot deformation temperature (HDT)1.8 MPa, 未退火，HDTISO 75-2/A210 °C
injectionTest ConditionTest MethodDOMO CHEM GERMANY/6LVG50H1 NC
drying time2.0 to 4.0 hr
Processing (melt) temperature260 to 280 °C
drying temperature75 to 85 °C
Temperature90 to 100 °C