Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC G-3130PH TEIJIN JAPAN
PANLITE®
Engineering accessories
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
Impact strength of simply supported beam without notchISO 17938 kJ/m²
Mechanical propertiesTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
Tensile modulusISO 527-2/15000 Mpa
bending strengthASTM D790/ISO 178135 kg/cm²(MPa)[Lb/in²]
tensile strength 断裂ISO 527-2/586.0 Mpa
Flexural modulusASTM D790/ISO 1786000 kg/cm²(MPa)[Lb/in²]
bending strengthISO 178135 Mpa
Flexural modulusISO 1786000 Mpa
Tensile strain断裂ISO 527-2/52.0 %
Tensile modulusASTM D638/ISO 5275000 kg/cm²(MPa)[Lb/in²]
elongation at breakASTM D638/ISO 5272.0 %
tensile strength ASTM D638/ISO 52786.0 kg/cm²(MPa)[Lb/in²]
Electrical performanceTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 3
Surface ResistivityASTM D257/IEC 60093>1.0E+15 Ω
dielectric strengthIEC 60243-135 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
relative permittivity100HzIEC 602503.50
Dissipation Factor100HzIEC 602501E-03
dielectric constantASTM D150/IEC 602503.50
Dielectric lossASTM D150/IEC 602500.0090
relative permittivity1MHzIEC 602503.50
Surface ResistivityIEC 60093>1.0E+15 ohms
Volume resistivityASTM D257/IEC 60093>1.0E+15 Ω.cm
Dissipation Factor1MHzIEC 602509E-03
otherTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
notes以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整。
Physical propertiesTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
Shrinkage rateASTM D9550.30-0.50 %
Water absorption rateASTM D570/ISO 620.12 %
flammabilityTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
UL flame retardant rating1.5mmUL 94V-2
physical property Test ConditionTest MethodTEIJIN JAPAN/G-3130PH
Water absorption rate23°C,24hrISO 620.12 %
Shrinkage rateMD:4.00mm内部方法0.10-0.30 %
TD:4.00mm内部方法0.30-0.50 %
Thermal performanceTest ConditionTest MethodTEIJIN JAPAN/G-3130PH
Heat distortion temperatureHDTASTM D648/ISO 75134 ℃（℉）
vicatASTM D1525/ISO R306138 ℃（℉）
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B134 °C
RTI Imp1.7mmUL 74680.0 °C
vicatISO 306/B50138 °C
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/A126 °C
RTI Elec1.7mmUL 74680.0 °C
Linear coefficient of thermal expansionMDISO 11359-23E-05 cm/cm/°C
RTI Str1.7mmUL 74680.0 °C
Linear coefficient of thermal expansionTDISO 11359-26E-05 cm/cm/°C
ASTM D696/ISO 113590.000030 mm/mm.℃