Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC RX2530 451118 COVESTRO THAILAND
Makrolon®
Automotive Applications,Lighting installation,electrical equipment
Flame retardant,High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 70.0 J |
| Charpy Notched Impact Strength | -30°C,完全断裂 | ISO 7391 | 14 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | 23°C,局部断裂 | ISO 7391 | 65 kJ/m² |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | NoBreak |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 60.0 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 5300 N |
| Charpy Notched Impact Strength | 23°C,局部断裂 | ISO 7391 | 70 kJ/m² |
| Impact strength of cantilever beam gap | -30°C,完全断裂 | ISO 7391 | 12 kJ/m² |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6200 N |
| hardness | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 118 Mpa |
| Electrical performance | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| Volume resistivity | 23°C | IEC 60093 | 1E+16 ohms·cm |
| Surface Resistivity | IEC 60093 | 1E+16 ohms |
| Mechanical properties | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| bending strength | 3.5%Strain,23°C | ISO 178 | 74.0 Mpa |
| Bending Strain | 23°C | ISO 178 | 7.0 % |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 67.0 Mpa |
| bending strength | 23°C | ISO 178 | 100 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/50 | 75.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 6.1 % |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 130 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
| flammability | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| FlashIgnitionTemperature | ASTM D1929 | 480 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| SelfIgnitionTemperature | ASTM D1929 | 550 °C |
| physical property | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| Shrinkage rate | TD | ISO 2577 | 0.60-0.80 % |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| Shrinkage rate | TD:2.00mm3 | ISO 294-4 | 0.65 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.12 % |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 15.0 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.30 % |
| Shrinkage rate | MD | ISO 2577 | 0.60-0.80 % |
| MD:2.00mm3 | ISO 294-4 | 0.60 % | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 16 g/10min |
| Thermal performance | Test Condition | Test Method | COVESTRO THAILAND/RX2530 451118 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 142 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 134 °C |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 122 °C |
| vicat | -- | ISO 306/B50 | 141 °C |
| ball-indentation hardness | 132°C | IEC 60695-10-2 | Pass |
| Glass Transition Temperature | ISO 11357-2 | 142 °C |