Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 LAMIGAMID® 307 SCHWARTZ GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| Impact strength of cantilever beam gap | kJ/m² | >6.0 >15 | |
| Suspended wall beam without notch impact strength | 无断裂 |
| hardness | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| ball-indentation hardness | MPa | 130 115 |
| Mechanical properties | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| compression stress | 5%应变 | MPa | 29.0 -- |
| coefficient of friction | 与钢-动态 | 0.040 0.080 | |
| Tensile modulus | MPa | 3000 2300 | |
| tensile strength | 屈服 | MPa | 65.0 45.0 |
| 断裂 | MPa | 100 40.0 | |
| coefficient of friction | 与钢-静态 | 0.31 -- | |
| Flexural modulus | MPa | 2500 2000 | |
| compression stress | 10%应变 | MPa | 46.0 -- |
| 20%应变 | MPa | 67.0 -- | |
| Tensile strain | 断裂 | % | >25 -- |
| Electrical performance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| dielectric strength | kV/mm | 50 20 | |
| Dissipation Factor | 0.030 -- | ||
| Surface Resistivity | ohms | 1E+12 1E+10 | |
| dielectric constant | 3.70 -- |
| physical property | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| density | g/cm³ | 1.13 -- | |
| Water absorption rate | 饱和,23°C | % | 7.0 -- |
| 23°C,24hr | % | 2.2 -- |
| Thermal performance | Test Condition | Test Method | SCHWARTZ GERMANY/LAMIGAMID® 307 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 200 -- |
| melting temperature | °C | 215 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 110 -- |
| specific heat | J/kg/°C | 1670 -- | |
| thermal conductivity | W/m/K | 0.25 -- | |
| Linear coefficient of thermal expansion | MD：20到100°C | cm/cm/°C | 7.0E-5到8.0E-5 -- |