PBT 1101H TORAY JAPAN
Toraycon®
Shell
Good appearance,Mineral reinforcement
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 20 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | ISO 2039-2 | 80 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.8 % |
| bending strength | 23°C | ISO 178 | 100 Mpa |
| Flexural modulus | 23℃ | ISO 178 | 4300 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 55.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 4300 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 4600 Mpa |
| tensile strength | 屈服, 23℃ | ISO 527-2 | 55.0 Mpa |
| Rockwell hardness | M 计秤 | ISO 2039-2 | 80 |
| Tensile modulus | 23℃ | ISO 527-2 | 4600 Mpa |
| Tensile strain | 断裂, 23℃ | ISO 527-2 | 1.8 % |
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 20 kJ/m² |
| bending strength | 23℃ | ISO 178 | 100 Mpa |
| flammability | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 1.7 % |
| MD:3.00mm4 | 内部方法 | 1.8 % | |
| MD: 3.00 mm | 内部方法 | 1.8 % | |
| TD: 3.00 mm | 内部方法 | 1.7 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/1101H |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 150 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 150 °C | |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 75.0 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C | |
| UL flame retardant rating | UL 94 | HB |