Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM NW-02LV JAPAN POLYPLASTIC
DURACON®
Electrical field、Electronic field、Fitness equipment、Automotive sector、Bottle cap
High sliding、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
Charpy Notched Impact Strength23°CISO 179/1eA5.9 kJ/m²
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
ColorNumberCF2001/CD3501
Mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
Wear factor0.98MPa,0.30m/sec4JISK7218<1.0 10^-8mm³/N·m
0.060MPa,0.15m/sec7JISK72181000 10^-8mm³/N·m
0.98MPa,0.30m/sec5JISK721819 10^-8mm³/N·m
0.060MPa,0.15m/sec6JISK7218400 10^-8mm³/N·m
Tensile modulusISO 527-22250 Mpa
coefficient of friction与钢-动态3JISK72180.17
Nominal tensile fracture strainISO 527-220 %
bending strengthISO 17868.0 Mpa
Flexural modulusISO 1782100 Mpa
coefficient of frictionDynamic2JISK72180.32
tensile strength ISO 527-252.0 Mpa
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
UL flame retardant ratingUL 94HB
physical property Test ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
Melt volume flow rate190°C/2.16kgISO 113318.0 cm3/10min
Shrinkage rateMD:2.00mmISO 294-42.0 %
Water absorption rate23°C,24hrISO 620.70 %
densityISO 11831.36 g/cm³
melt mass-flow rate190°C/2.16kgISO 113320 g/10min
Shrinkage rateTD:2.00mmISO 294-41.8 %
Thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/NW-02LV
Linear coefficient of thermal expansionTD:23to55°C内部方法1.2E-04 cm/cm/°C
MD:23到55°C内部方法1.2E-04 cm/cm/°C
Heat distortion temperature1.8MPa,未退火,HDTISO 75-2/A80.0 °C