EPE ELITE™ 5400G DOW USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| film | Test Condition | Test Method | DOW USA/ELITE™ 5400G |
|---|---|---|---|
| film strength | MD | ASTM D882 | 83.6 J/cm³ |
| tensile strength | TD:断裂 | ASTM D882 | 36.3 MPa |
| Thin film puncture strength | 内部方法 | 6.67 J | |
| elongation | MD:断裂 | ASTM D882 | 450 % |
| tensile strength | MD:断裂 | ASTM D882 | 38.5 MPa |
| Thin film puncture strength | 内部方法 | 32.3 J/cm³ | |
| Secant modulus | 2%正割,TD | ASTM D882 | 209 MPa |
| 1%正割,MD | ASTM D882 | 218 MPa | |
| Thin film puncture strength | 内部方法 | 68.9 N | |
| Elmendorf tear strength | MD | ASTM D1922 | 280 g |
| Dart impact | ASTM D1709B | 1000 g | |
| Secant modulus | 2%正割,MD | ASTM D882 | 188 MPa |
| tensile strength | TD:屈服 | ASTM D882 | 10.5 MPa |
| film thickness | 25 µm | ||
| Secant modulus | 1%正割,TD | ASTM D882 | 251 MPa |
| Elmendorf tear strength | TD | ASTM D1922 | 600 g |
| film strength | TD | ASTM D882 | 95.1 J/cm³ |
| elongation | TD:断裂 | ASTM D882 | 630 % |
| tensile strength | MD:屈服 | ASTM D882 | 10.4 MPa |
| optical performance | Test Condition | Test Method | DOW USA/ELITE™ 5400G |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 32 |
| Haze ratio | ASTM D1003 | 20 % |
| physical property | Test Condition | Test Method | DOW USA/ELITE™ 5400G |
|---|---|---|---|
| density | ASTM D792 | 0.916 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 1.0 g/10min |
| Thermal performance | Test Condition | Test Method | DOW USA/ELITE™ 5400G |
|---|---|---|---|
| vicat | ASTM D1525 | 104 °C | |
| melting temperature | 内部方法 | 123 °C |