PC HP1R-1H112 SABIC INNOVATIVE CANADA
LEXAN™
medical care、medicine、Medical/nursing supplies
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HP1R-1H112 |
|---|---|---|---|
| Simple supported beam without notch impact strength 8 | -30°C | ISO179/1eU | 无断裂 |
| 23°C | ISO179/1eU | 无断裂 | |
| Unscented Izod Impact Strength 9 | 23°C | ISO180/1U | 无断裂 |
| Impact strength of simply supported beam gap 8 | 23°C | ISO179/1eA | 65 kJ/m² |
| -30°C | ISO179/1eA | 10 kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 54.0 J |
| Unscented Izod Impact Strength 9 | -30°C | ISO180/1U | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HP1R-1H112 |
|---|---|---|---|
| tensile strength | 断裂 | ISO527-2/50 | 50.0 Mpa |
| Tensile modulus | --3 | ASTMD638 | 2370 Mpa |
| elongation | 屈服 | ISO527-2/50 | 6.0 % |
| Bending stress | --6,7 | ISO178 | 90.0 Mpa |
| Flexural modulus | 50.0mm跨距5 | ASTMD790 | 2300 Mpa |
| Bending stress | 屈服,50.0mm跨距5 | ASTMD790 | 93.0 Mpa |
| tensile strength | 屈服4 | ASTMD638 | 62.0 Mpa |
| 屈服 | ISO527-2/50 | 63.0 Mpa | |
| Tensile modulus | -- | ISO527-2/1 | 2350 Mpa |
| elongation | 断裂4 | ASTMD638 | 120 % |
| 断裂 | ISO527-2/50 | 70 % | |
| 屈服4 | ASTMD638 | 6.0 % | |
| Flexural modulus | --6 | ISO178 | 2300 Mpa |
| tensile strength | 断裂4 | ASTMD638 | 65.0 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HP1R-1H112 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50到0.70 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| 饱和,23°C | ISO62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTMD1238 | 28 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 26.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/HP1R-1H112 |
|---|---|---|---|
| MD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C | |
| vicat | -- | ASTMD152511,ISO306/B5011 | 139 °C |
| Heat distortion temperature | 1.8MPa,未退火,100mm跨距10 | ISO75-2/Ae | 121 °C |
| TD:-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm | ASTMD648 | 126 °C |
| vicat | -- | ISO306/B120 | 140 °C |
| MD:23到80°C | ISO11359-2 | 7E-05 cm/cm/°C | |
| TD:-40到95°C | ASTME831 | 6.8E-05 cm/cm/°C |