Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PA66 HTN54G15HSLR DUPONT USA

Zytel®

building materials,Industrial applications,Automotive interior parts,Electronic field,Electrical field

Glass fiber reinforced,Toughening,Filler: Glass fiber reinf,15% filler by weight

Plastic Datasheets

thermal performance	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	277 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	230 °C
Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	7E-05 cm/cm/°C
		MD：--	ISO 11359-2	3.4E-05 cm/cm/°C
		MD：-40to23°C	ISO 11359-2	3.4E-05 cm/cm/°C
		TD：--	ISO 11359-2	7.3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	300 °C

mechanical properties	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
Bending modulus		ISO 178	4900 Mpa
bending strength		ISO 178	210 Mpa
Tensile modulus		ISO 527-2	5500 Mpa
Tensile strain	Break	ISO 527-2	3.5 %
tensile strength	Break	ISO 527-2	125 Mpa

Electrical performance	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
Volume resistivity		IEC 60093	1E+15 ohms·cm

Physical properties	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
density		ISO 1183	1.25 g/cm³
Shrinkage rate	MD	ISO 294-4	0.40 %
Shrinkage rate		TD	ISO 294-4	0.70 %

impact performance	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0 kJ/m²
Charpy Notched Impact Strength		-40°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60 kJ/m²

flammability	Test Condition	Test Method	DUPONT USA/HTN54G15HSLR
Burning rate	1.00mm	ISO 3795	<100 mm/min
FMVSS flammability		FMVSS302	B
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
		1.5mm	IEC 60695-11-10,-20	HB
		0.8mm	UL 94	HB
		1.5mm	UL 94	HB