Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 BGZ-15/2 EMS-CHEMIE SWITZERLAND
Grilon®
Automotive sector、Shell、electrical machinery、Industrial machinery、Electronic field、Electrical field
Glass fiber reinforced、Electrical performance、Antichemical、wear resistant、Thermal stability、High impact resistance、high strength、High hardness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Impact strength of simply supported beam gap | -30℃ -30°C | ISO 179/1eA | 11 kJ/m² |
| 23℃ 23°C | ISO 179/1eA | 20 kJ/m² | |
| Impact strength of simply supported beam without notch | -30℃ -30°C | ISO 179/1eU | 70 kJ/m² |
| 23℃ 23°C | ISO 179/1eU | 75 kJ/m² |
| Mechanical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 5300 Mpa | |
| Tensile strain | 断裂 断裂 | ISO 527-2 | 5 % |
| Tensile strength | 断裂 断裂 | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 100000000000000 ohms·cm | |
| Dielectric strength | IEC 60243-1 | 40 KV/mm | |
| Surface resistivity | IEC 60093 | -- ohms | |
| Compared to the leakage trace index | IEC 60112 | -- V |
| Flame retardant performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Flammability level | 0.8 mm 0.8 mm | IEC 60695-11-10, -20 | HB |
| physical property | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Shrinkage rate | TD Across Flow | ISO 294-4 | 0.7 % |
| MD Flow | ISO 294-4 | 0.2 % | |
| Water absorption rate | 饱和，23℃ Saturation, 73°F | ISO 62 | 8 % |
| 平衡，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 2 % | |
| density | ISO 1183 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | EMS-CHEMIE SWITZERLAND/BGZ-15/2 |
|---|---|---|---|
| Continuous use temperature | -- -- 4 4 | 内部方法 | 160 °C |
| 熔融温度 Melting Temperature 5 5 | ISO 11357-3 | 222 °C | |
| -- -- 3 3 | ISO 2578 | 90.0 到 120 °C | |
| TD Transverse | ISO 11359-2 | 0.00012 1/℃ | |
| Hot deformation temperature | 1.8 MPa，未退火 264 psi, Unannealed | ISO 75-2/A | 190 °C |
| 8.0 MPa，未退火 1160 psi, Unannealed | ISO 75-2/C | 55 °C | |
| MD 流动 | ISO 11359-2 | 0.000050 1/℃ |