PBT 357U-1001 SABIC INNOVATIVE US
VALOX™
Electrical field、Electronic field、Electrical appliances、medicine、Medical supplies、Nursing supplies、Plastic bag、Liquid handling、Lawn equipment、Garden equipment、Non specific food、Outdoor applications、Industrial applications、Household goods、Architectural application、Lighting applications
Flame retardant、UV resistance、Impact modification
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| Dart impact | 23°C7 | ASTM D3029 | 43.4 J |
| 23°C | ASTM D3029 | 43.4 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 117 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.2E+16 ohms·cm | |
| Dissipation Factor | 100Hz | ASTM D150 | 3E-03 |
| 1MHz | ASTM D150 | 0.030 | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| dielectric constant | 1MHz | ASTM D150 | 3.20 |
| 100Hz | ASTM D150 | 3.20 | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| dielectric strength | 1.60mm,inOil | ASTM D149 | 25 KV/mm |
| 3.20mm,inOil | ASTM D149 | 19 KV/mm | |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
| arc resistance | ASTM D495 | PLC6 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 110 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 82.7 Mpa |
| tensile strength | 断裂 | ASTM D638 | 48.3 Mpa |
| 屈服 | ASTM D638 | 48.3 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2070 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 82.7 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| UL flame retardant rating | 0.64mm | UL 94 | V-0 |
| 0.46mm | UL 94 | HB | |
| 3.0mm | UL 94 | 5VA | |
| Limiting Oxygen Index | ASTM D2863 | 30 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| Water absorption rate | 24hr | ASTM D570 | 0.080 % |
| Shrinkage rate | TD3 | 内部方法 | 1.2-1.6 % |
| TD4 | 内部方法 | 0.90-1.3 % | |
| Outdoor applicability | UL 746C | f2 | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 8.00 cm3/10min |
| Specific volume | ASTM D792 | 0.750 cm³/g | |
| Shrinkage rate | MD3 | 内部方法 | 1.0-1.4 % |
| MD4 | 内部方法 | 0.80-1.1 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/357U-1001 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 98.9 °C |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9.2E-05 cm/cm/°C |
| MD：60到138°C | ASTME831 | 1.2E-04 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 138 °C |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C | |
| RTI Elec | UL 746 | 120 °C |