PBT B 4406 G6(2) BK BASF GERMANY
Ultradur®
Laptop case、Switch panel、Electrical components
Glass fiber reinforced、Flame retardant、Filler: Glass fiber reinf、30% filler by weight、30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 50 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| dielectric constant | 100Hz | IEC 60250 | 3.90 |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 2E-03 |
| dielectric constant | 1MHz | IEC 60250 | 3.90 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.1 % |
| bending strength | 23°C | ISO 178 | 220 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 11500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 140 Mpa |
| flammability | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | |
| 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 22.0 cm3/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| density | ISO 1183 | 1.68 g/cm³ | |
| Viscosity value | 降低的粘度 | ISO 1628 | 98.0 ml/g |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4406 G6(2) BK |
|---|---|---|---|
| RTI Imp | 0.75mm | UL 746 | 130 °C |
| RTI Str | 0.75mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 130 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 205 °C | |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| 3.0mm | UL 746 | 140 °C | |
| RTI Imp | 3.0mm | UL 746 | 130 °C |
| melting temperature | ISO 3146 | 223 °C | |
| RTI Elec | 0.75mm | UL 746 | 140 °C |