POM Copolymer LUVOCOM® 80-8588/L LEHVOSS Group
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 80-8588/L |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1fU | 75 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 80-8588/L |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2200 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 46.0 MPa |
| Tensile strain | 屈服 | ISO 527-2 | 10 % |
| Bending Strain | ISO 178 | 12 % | |
| Flexural modulus | ISO 178 | 1800 MPa | |
| bending strength | ISO 178 | 65.0 MPa |
| Electrical performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 80-8588/L |
|---|---|---|---|
| insulation resistance | IEC 60167 | >1.0E+12 ohms |
| physical property | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 80-8588/L |
|---|---|---|---|
| Shrinkage rate | DIN 16901 | 1.6to2.2 % | |
| Water absorption rate | 23°C,24hr | 0.15 % | |
| density | ISO 1183 | 1.48 g/cm³ |
| Thermal performance | Test Condition | Test Method | LEHVOSS Group/LUVOCOM® 80-8588/L |
|---|---|---|---|
| Continuous use temperature | UL 746B | 100 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |
| vicat | ISO 306/A | 145 °C | |
| maximum service temperature | ShortTerm | 120 °C |