Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS GP-22 BK BASF BELGIUM
Terluran®
Shell、TV casing、small home appliances
High mobility、High rigidity、Medium impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 22 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 59 J/m |
| 23°C | ASTM D256 | 300 J/m | |
| -18°C | ASTM D256 | 100 J/m | |
| Charpy Notched Impact Strength | -30°C | ISO 179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 100 kJ/m² |
| 23°C | ISO 179 | 180 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 26 kJ/m² |
| -30°C | ISO 180/A | 8.0 kJ/m² |
| hardness | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 103 |
| ball-indentation hardness | ISO 2039-1 | 97.0 Mpa |
| Mechanical properties | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2300 Mpa | |
| ISO 527-2 | 2300 Mpa | ||
| elongation | 断裂 | ASTM D638 | 2.6 % |
| bending strength | ISO 178 | 65.0 Mpa | |
| tensile strength | 屈服,23°C | ISO 527-2 | 45.0 Mpa |
| bending strength | ASTM D790 | 65.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 2.6 % |
| tensile strength | 屈服,23°C | ASTM D638 | 45.0 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 10 % |
| Flexural modulus | ASTM D790 | 2300 Mpa |
| Electrical performance | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | 1E+15 ohms·cm | ||
| relative permittivity | 100Hz | IEC 60250 | 2.90 |
| Dissipation Factor | 100Hz | IEC 60250 | 4.8E-03 |
| dielectric constant | 1.00mm,1MHz | ASTM D150 | 2.80 |
| relative permittivity | 1MHz | IEC 60250 | 2.80 |
| Surface Resistivity | IEC 60093 | 1E+13 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 7.9E-03 |
| optical performance | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| Yellowness Index | DIN 6167 | 13 YI |
| physical property | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.5 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40-0.70 % |
| Water absorption rate | 饱和,23°C | ASTM D570 | 1.0 % |
| Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.22 % |
| Melt volume flow rate | 230°C/3.8kg | ASTM D1238 | 4.80 cm3/10min |
| Water absorption rate | 饱和,23°C | ISO 62 | 1.0 % |
| density | ASTM D792 | 1.04 g/cm³ | |
| ISO 1183 | 1.04 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 19 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 19.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | BASF BELGIUM/GP-22 BK |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.17 W/m/K | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 77.8 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 90.6 °C | |
| 1.8MPa,退火，HDT | ASTM D648 | 98.9 °C | |
| vicat | -- | ISO 306/A50 | 105 °C |
| Heat distortion temperature | 1.8MPa,退火，HDT | ISO 75-2/A | 94.0 °C |
| vicat | -- | ISO 306/B50 | 96.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.0E-5to1.1E-4 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,退火，HDT | ASTM D648 | 104 °C |
| 0.45MPa,Annealed，HDT | ISO 75-2/B | 99.0 °C |