Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2300EPR-7301 SABIC INNOVATIVE US
ULTEM™
Automotive Applications、Fitness equipment
Glass fiber reinforced、Flame retardant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| ReverseNotchIzodImpact | 3.20mm | ASTMD256 | 490 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| Rockwell hardness | M级 | ASTMD785 | 114 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| High arc combustion index (HAI) | HAI | UL746 | PLC 4 |
| Volume resistivity | ASTMD257 | 3E+16 ohms·cm | |
| Dissipation Factor | 1kHz | ASTMD150 | 1.5E-03 |
| dielectric constant | 1kHz | ASTMD150 | 3.70 |
| Arc resistance 6 | ASTMD495 | PLC6 | |
| Dissipation Factor | 2.45GHz | ASTMD150 | 5.3E-03 |
| dielectric strength | 1.60mm,在油中 | ASTMD149 | 30 KV/mm |
| Hot wire ignition (HWI) | HWI | UL746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 3 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL746 | PLC 4 |
| dielectric strength | 1.60mm,inAir | ASTMD149 | 25 KV/mm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 3.0 % |
| Flexural modulus | 100mmSpan | ASTMD790 | 8960 Mpa |
| tensile strength | 屈服 | ASTMD638 | 169 Mpa |
| 断裂 | ASTMD638 | 159 Mpa | |
| Flexural Strength4 | Break,100mmSpan | ASTMD790 | 228 Mpa |
| Tensile modulus | ASTMD638 | 9310 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| UL flame retardant rating | 1.2mm | UL94 | 5VA |
| Limiting Oxygen Index | ASTMD2863 | 50 % | |
| NBSSmokeDensity-Flaming,Ds,4min | ASTME662 | 1.60 | |
| UL flame retardant rating | 0.25mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.40 % |
| Water absorption rate | 平衡,23°C | ASTMD570 | 0.90 % |
| melt mass-flow rate | 337°C/6.6kg | ASTMD1238 | 5.3 g/10min |
| Water absorption rate | 24hr | ASTMD570 | 0.16 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/2300EPR-7301 |
|---|---|---|---|
| vicat | ASTMD15255 | 228 °C | |
| RTI Str | UL746 | 180 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 210 °C |
| RTI Elec | UL746 | 180 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 212 °C |
| RTI Imp | UL746 | 170 °C | |
| Linear thermal expansion coefficient | MD：-20to150°C | ASTME831 | 2E-05 cm/cm/°C |