PC DX10311-701 SABIC INNOVATIVE NANSHA
--
--
Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX10311-701 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 750 J/m |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/2U | 57 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX10311-701 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 1.9E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 6.4E-05 cm/cm/°C | |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 128 °C |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX10311-701 |
|---|---|---|---|
| fracture | ISO 527-2/5 | 119 Mpa | |
| ASTM D638 | 2.6 % | ||
| --4 | ISO 178 | 7730 Mpa | |
| --6 | ISO 178 | 181 Mpa | |
| --5 | ISO 178 | 182 Mpa | |
| fracture | ASTM D638 | 117 Mpa | |
| --1 | ASTM D638 | 8340 Mpa | |
| fracture | ISO 527-2/5 | 2.7 % |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/DX10311-701 |
|---|---|---|---|
| Melt volume flow rate | 300°C/5.0kg | ISO 1133 | 37.0 cm3/10min |
| shrinkage rate | TD:3.20mm | 内部方法 | 0.20-0.40 % |
| MD:3.20mm | 内部方法 | 0.10-0.30 % |