LCP SUMIKASUPER® E4008 MR SUMITOMO JAPAN

Unit Price:
$10242 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 130****13

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	内部方法	1.3	%
Modeling Shrinkage	Modeling Shrinkage	流量	内部方法	0.10	%
Moisture Absorption	Saturation	ASTM D570	0.020	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength		ASTM D638	150	Mpa
Tensile Elongation	Break	ASTM D638	5.0	%
Flexural Modulus	23°C	ASTM D790	12300	Mpa
Flexural Modulus	Flexural Modulus	200°C	ASTM D790	6300	Mpa
Flexural Strength	23°C	ASTM D790	139	Mpa
Flexural Strength	Flexural Strength	200°C	ASTM D790	39.0	Mpa
Shearing Strength		ASTM D732	52.0	Mpa
Poisson Ratio		ASTM D785	0.49

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load	1.8 MPa, Unannealed	ASTM D648	313	°C
Coefficient of Linear Thermal Expansion	Flow : 150°C	内部方法	1.4E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion	Coefficient of Linear Thermal Expansion	Across Flow : 150°C	内部方法	6.2E-5	cm/cm/°C
Thermal Conductivity		JIS R2618	0.57	W/m/K

Electrical Properties	Test Condition	Test Method	Test Result	Unit
Volume Resistivity		ASTM D257	1.0E+15	ohms·cm
Dielectric Constant	1 kHz	ASTM D150	4.50
Dielectric Constant	Dielectric Constant	1 MHz	ASTM D150	3.90
Dissipation Factor	1 kHz	ASTM D150	0.018
Dissipation Factor	Dissipation Factor	1 MHz	ASTM D150	0.034
Arc Resistance		ASTM D495	130	sec
Comparative Tracking Index		IEC 60112	145	V

Injection	Test Result	Unit
Drying Temperature	130	°C
Drying Time	4.0 到 24	hr
Rear Temperature	330 到 350	°C
Middle Temperature	350 到 370	°C
Front Temperature	370 到 390	°C
Nozzle Temperature	370 到 390	°C
Processing (Melt) Temp	380	°C
Mold Temperature	40 到 160	°C
Injection Pressure	120 到 160	Mpa
Injection Rate	中等偏快
Holding Pressure	40.0 到 60.0	Mpa
Back Pressure	1.00 到 5.00	Mpa
Screw Speed	50 到 100	rpm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	6.40 mm	ASTM D256	520	J/m

Hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTM D785	91

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.30 mm, NC, BK	UL 94	V-0
Oxygen Index		ISO 527-1,-2(JIS K7161,7162)	48	%
Soldering Resistance		内部方法	330	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.