PC PANLITE® ML-3206ZT TEIJIN JAPAN
33
- Unit Price:
- $4511 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 33.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 130****13
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 300℃ | ISO 1133 | 18 | cm310min |
| Modeling Shrinkage | MD | In-house method | 0.5-0.7 | % |
| TD | In-house method | 0.5-0.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength(Yield) | 50mm/min | ISO 527-1,2 | 61 | Mpa |
| Tensile Strength(Break) | 50mm/min | ISO 527-1 | 68 | Mpa |
| Tensile Elongation (Break) | 50mm/min | ISO 527-1 | 105 | % |
| Flexural Modulus | 2mm/min | ISO 178 | 2400 | Mpa |
| Flexural Strength | 2mm/min | ISO 178 | 99 | Mpa |
| Notched Impact Strength | Notched | ISO 179 | 10 | kJ/m² |
| Tensile Elongation (Break) | ASTM D638/ISO 527 | 120 | % | |
| Tensile Modulus | ASTM D638/ISO 527 | 66 | kg/cm²(MPa)[Lb/in²] | |
| Tensile Strength | ASTM D638/ISO 527 | 61 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Modulus | ASTM D790/ISO 178 | 2300 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 96 | kg/cm²(MPa)[Lb/in²] | |
| Charpy Impact Strength | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in | |
| Notched Izod Impact Strength | ASTM D256/ISO 179 | 25 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile Elongation (Break) | ASTM D638/ISO 527 | 120 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.80MPa | ISO 75-1,2 | 129 | °C |
| 线膨胀系数，MD | ISO 11359-2 | 0.7 | X10-4/℃ | |
| TD | ISO 11359-2 | 0.7 | X10-4/℃ | |
| Flame Rating | 1.0mm/3.0mm | UL94 | V-2 | |
| Burning Rate | UL94 | V-2（相当） | ||
| Heat Deflection Temperature | ASTM D648/ISO 75 | 134 | ℃（℉） | |
| ASTM D648/ISO 75 | 129 | ℃（℉） | ||
| Coefficient of Linear Thermal Expansion | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | ASTM D1003/ISO 13468 | 2MM 86% | % | |
| 1.5mmt | JIS K7136 | 85 | % | |
| Particle Size Distribution | 2.0mmt | In-house method | 17 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.