Material Properties
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | -- | ASTMD792 | 1.08 | g/cm³ |
| Density / Specific Gravity | 23°C | ISO1183 | 1.08 | g/cm³ |
| Modeling Shrinkage | | ISO294-4 | 0.30到0.70 | % |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238,ISO1133 | 3.0 | g/10min |
| Mechanical | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield | ISO527-2/50 | 42.0 | Mpa |
| Tensile Stress | Break | ISO527-2/50 | 33.0 | Mpa |
| Tensile Stress | --3 | ASTMD638 | 39.7 | Mpa |
| Tensile Elongation | Break3 | ASTMD638 | 40 | % |
| Tensile Elongation | Break | ISO527-2/50 | 40 | % |
| Flexural Modulus | --4 | ASTMD790 | 1900 | Mpa |
| Flexural Modulus | --5 | ISO178 | 1900 | Mpa |
| Flexural Strength | --4 | ASTMD790 | 53.9 | Mpa |
| Flexural Strength | --5 | ISO178 | 57.0 | Mpa |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8MPa,Annealed | ISO75-2/A | 97.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed | ASTMD648 | 88.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 77.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Annealed | ASTMD648 | 99.0 | °C |
| Vicat Softening Temperature | -- | ASTMD15256 | 105 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 104 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 96.0 | °C |
| Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Impact | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179 | 7.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179 | 14 | kJ/m² |
| Notched Izod Impact Strength | 23°C,3.20mm | ASTMD256 | 150 | J/m |
| Notched Izod Impact Strength | 23°C,6.40mm | ASTMD256 | 160 | J/m |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 7.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 14 | kJ/m² |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 107 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.5mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.