Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.2 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | 厚度3mm | ASTM D-1003 | 88 | % |
Index of Refraction | | ASTM D-542 | 1.585 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ASTM D-785 | 77 | M标度 |
Tensile Elongation | Yield点,- | ASTM D-638 | 6 | - |
Tensile Elongation | Break点,- | ASTM D-638 | 140 | - |
Flexural Modulus | | ASTM D-790 | 2230(22700) | MPa(Kgf/cm |
Tensile Strength | Yield点,- | ASTM D-638 | 61(620) | MPa(Kgf/cm |
Tensile Strength | Break点,- | ASTM D-638 | 81(830) | MPa(Kgf/cm |
Tensile Modulus | | ASTM D-638 | 2120(21600) | MPa(Kgf/cm |
Flexural Strength | | ASTM D-790 | 90(915) | MPa(Kgf/cm |
Compressive Strength | | ASTM D-695 | 76(770) | MPa(Kgf/cm |
Notched Izod Impact Strength | 艾氏、带Notched厚度6.4mm | ASTM D-256 | 140(14) | j/m(kgf.cm/cm) |
Notched Izod Impact Strength | 艾氏、带Notched厚度3.2mm | ASTM D-256 | 880(90) | j/m(kgf.cm/cm) |
Tensile Modulus | | ASTM D638/ISO 527 | 2120(21600) | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 61(620)屈服 81(830)断裂 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 6 | % |
Rockwell Hardness | | ASTM D785 | M-77 | |
Flexural Modulus | | ASTM D790/ISO 178 | 2230(22700) | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 90(915) | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation (Break) | | ASTM D638/ISO 527 | 140 | % |
Charpy Impact Strength | | ASTM D256/ISO 179 | 140(14) | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Coefficient of Linear Thermal Expansion | Flow (Across Flow ) | ASTM D-696 | 7 | |
Heat Deflection Temperature | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 143 | °C |
Temperature Index | 电学式,厚度1.47mm | UL 746B | 125 | °C |
Temperature Index | 冲击式,厚度1.47mm | UL 746B | 115 | °C |
Temperature Index | 非冲击式,厚度1.47mm | UL 746B | 125 | °C |
Heat Deflection Temperature | 负荷1.813MPa(18.6kgf/cm) | ASTM D-648 | 143 | °C |
Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 7X10^-5 | mm/mm.℃ |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | CTI | IEC 112 | 300 | V |
Arc Resistance | | ASTM D-495 | 110 | secc |
Dissipation Factor (Tangent) | 60Hz(10 | ASTM D-150 | 0.0004(0.009) | |
Arc Resistance | | ASTM D495/IEC 60112 | 110 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 3 | Ω.cm |
Volume Resistivity | | ASTM D-257 | 3 | |
Insulation Resistance | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm |
Dielectric Constant | 60Hz(10 | ASTM D-150 | 2.95(2.9) | |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow (Across Flow ) | ASTM D-955 | 0.5~0.7 | % |
Optical | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | | ASTM D1003/ISO 13468 | 88 | % |
Index of Refraction | | ASTM D542/ISO 489 | 1.585 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr,in 23℃ | ASTM D-570 | 0.20 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.