Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 10 | g/10min |
| Density | | ASTM D792/ISO 1183 | 1.2 | |
| Modeling Shrinkage | | ASTM D955 | 0.6-0.8 | % |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.30 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation?(Break) | | ASTM D638/ISO 527 | ＞50 | % |
| Tensile Modulus | | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | | ASTM D638/ISO 527 | ＞66 | % |
| Charpy impact strength | | ASTM D256/ISO 179 | N | kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 90 | kg·cm/cm(J/M)ft·lb/in |
| Izod notch impact strength | | ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | UL94 | V-2 | |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 138 | ℃（℉） |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 125 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 145 | ℃（℉） |
| Linear expansion coefficient | | ASTM D696/ISO 11359 | 0.65 | mm/mm.℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | 1E16 | Ω |
| Dielectric Constant | | ASTM D150/IEC 60250 | 3.1 | |
| Dielectric Constant | | ASTM D150/IEC 60250 | 3.0 | |
| Arc Resistance | | ASTM D495/IEC 60112 | 275 | |
| Volume Resistivity | | ASTM D257/IEC 60093 | 1E14 | Ω.cm |
| Dielectric loss | | ASTM D150/IEC 60250 | 5 | |
| Dielectric loss | | ASTM D150/IEC 60250 | 90 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | | ASTM D1003/ISO 13468 | 89 | % |
| Refractive index of light | | ASTM D542/ISO 489 | 1.586 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.