Material Properties
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.08 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.3 | % |
| Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 19~23 | g/10min |
| Mechanical | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact Strength | 12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | kg.cm/cm | ASTM D-256 | |
| Impact Strength | 3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | kg.cm/cm | ASTM D-256 | |
| Tensile Strength | | ASTM D638/ISO 527 | 490（屈服）380（断裂） | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | | ASTM D638/ISO 527 | 3.5 | % |
| Rockwell Hardness | | ASTM D785 | R-115 | |
| Rockwell Hardness | 23℃ | R | ASTM D-785 | 115 |
| Flexural Modulus | | ASTM D790/ISO 178 | 23500 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 780 | kg/cm²(MPa)[Lb/in²] |
| Tensile Strength (Yield) | 23℃ | kg/cm | ASTM D-638 | 490 |
| Tensile Strength (Yield) | 23℃ | % | ASTM D-638 | |
| Tensile Strength (Break) | 23℃ | % | ASTM D-638 | |
| Tensile Strength (Break) | 23℃ | kg/cm | ASTM D-790 | |
| Tensile Strength(Break) | 23℃ | kg/cm | ASTM D-638 | 380 |
| Flexural Stress | 23℃ | kg/cm | ASTM D-790 | 780 |
| Notched Izod Impact Strength | | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in |
| Notched Izod Impact Strength | | ASTM D256/ISO 179 | 6 | kg·cm/cm(J/M)ft·lb/in |
| Tensile Elongation (Break) | | ASTM D638/ISO 527 | 30 | % |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability | | | UL-94 | |
| Burning Rate | | UL94 | HB | |
| Heat Deflection Temperature | | ASTM D648/ISO 75 | 89 | ℃（℉） |
| Heat Deflection Temperature | 18.56kg/cm | ℃ | ASTM D-648 | 89 |
| Coefficient of Linear Thermal Expansion | | | ASTM D-696 | |
| Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 1.2x10^-4 | mm/mm.℃ |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 浸入23℃水中24hr | % | ASTM D-570 | 0.3 |
| Melt Mass-Flow Rate | 220℃/10.0kg | g/10min | ASTM D-1238 | |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 220℃ | ×10 | 插入式粘度计 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.