Material Properties
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.2 | |
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.3 | % |
| Mechanical | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] |
| Tensile Elongation | | ASTM D638/ISO 527 | 6.0 | % |
| Flexural Modulus | | ASTM D790/ISO 178 | 65 | kg/cm²(MPa)[Lb/in²] |
| Charpy Impact Strength | | ASTM D256/ISO 179 | N | kg·cm/cm(J/M)ft·lb/in |
| Tensile Elongation (Break) | | ASTM D638/ISO 527 | >50 | % |
| Notched Izod Impact Strength | | ASTM D256/ISO 179 | 70P（C） | kg·cm/cm(J/M)ft·lb/in |
| Optical | Test Condition | Test Method | Test Result | Unit |
|---|
| Transmittance | | ASTM D1003/ISO 13468 | 89 | % |
| Index of Refraction | | ASTM D542/ISO 489 | 1.586 | |
| Thermal | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | | ASTM D648/ISO 75 | 125 | ℃（℉） |
| Heat Deflection Temperature | | ASTM D648/ISO 75 | 138 | ℃（℉） |
| Melting Temperature | | | 280 | ℃（℉） |
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 145 | ℃（℉） |
| Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 0.65 | mm/mm.℃ |
| Electrical | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTM D257/IEC 60093 | 1E16 | Ω |
| Dielectric Constant | | ASTM D150/IEC 60250 | 3.1 | |
| Dielectric Constant | | ASTM D150/IEC 60250 | 3.0 | |
| Arc Resistance | | ASTM D495/IEC 60112 | 275 | |
| Volume Resistivity | | ASTM D257/IEC 60093 | 1E14 | Ω.cm |
| Dissipation Factor | | ASTM D150/IEC 60250 | 5 | |
| Dissipation Factor | | ASTM D150/IEC 60250 | 90 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.