Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTMD792 | 1.05 | g/cm³ |
Density | 23°C | ISO1183 | 1.05 | g/cm³ |
Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 1.9 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 19 | g/10min |
Melt Mass-Flow Rate | 200°C/5.0kg | ISO1133 | 1.9 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 19 | g/10min |
Modeling Shrinkage | MD | 内部方法 | 0.40to0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | 23°C | ASTMD638 | 47.6 | Mpa |
Tensile Stress | 屈服,23°C | ISO527-2 | 48.0 | Mpa |
Flexural Modulus | 23°C | ASTMD790 | 2650 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2650 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 79.4 | Mpa |
Flexural Stress | 23°C | ISO178 | 79.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTMD15253 | 100 | °C |
Vicat Softening Temperature | | ISO306/A | 100 | °C |
Deflection Temperature Under Load? | 1.8MPa,退火 | ISO75-2/A | 95.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 85.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 95.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C,6.35mm | ISO180 | 200 | J/m |
Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 200 | J/m |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R计秤,23°C | ASTMD785 | 110 | |
Rockwell Hardness | R计秤,23°C | ISO2039-2 | 110 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm,AllColors | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.