Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.18mm | ASTMD955 | 0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.37 | % |
| Moisture Absorption | Equilibrium | ASTMD570 | 1.1 | % |
| Melt Mass-Flow Rate | 365°C/5.0kg | ASTMD1238 | 20to28 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.29 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength | 5.0%Strain,3.18mm | ASTMD790 | 91.0 | Mpa |
| Tensile Modulus | 3.18mm | ASTMD638 | 2340 | Mpa |
| Tensile Strength | 3.18mm | ASTMD638 | 69.6 | Mpa |
| Tensile Elongation | Yield,3.18mm | ASTMD638 | 7.2 | % |
| Tensile Elongation | Break,3.18mm | ASTMD638 | 60to120 | % |
| Flexural Modulus | 3.17mm | ASTMD790 | 2410 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.18mm | ASTMD648 | 207 | °C |
| Linear thermal expansion coefficient | MD：3.18mm | ASTMD696 | 5.6E-05 | cm/cm/°C |
| Glass Transition Temperature | | DSC | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | 3.18mm | ASTMD257 | 9E+15 | ohms·cm |
| Dielectric Constant | 3.18mm,60Hz | ASTMD150 | 3.44 | |
| Dielectric Strength | 0.0254mm | ASTMD149 | >200 | KV/mm |
| Dielectric Strength | 3.18mm | ASTMD149 | 15 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 3.17mm | ASTMD256 | 690 | J/m |
| TensileImpactStrength | 3.18mm | ASTMD1822 | 399 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | | ASTMD542 | 1.672 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.76mm | UL94 | V-0 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| SteamSterilization-w/Morpholine4 | | | >1000 | cycles |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.