PA6/66 Ultramid® C3U BK BASF GERMANY

Unit Price:
$4794 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
51.6MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD：3.18mm		0.80	%
Moisture Absorption	Saturation	ASTMD570	8.5	%
	Moisture Absorption	Saturation,23°C	ISO62	8.5	%
		Moisture Absorption	Equilibrium,50%RH	ASTMD570	2.9	%
		Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	2.9	%
Melt Volume flow Rate	275°C/5.0kg	ISO1133	140	cm3/10min
Density / Specific Gravity		ASTMD792	1.16	g/cm³
Density / Specific Gravity	Density / Specific Gravity		ISO1183	1.16	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield,23°C	ASTMD638	83.0	Mpa
Nominal Tensile Strain at Break	23°C	ISO527-2	6.0	%
Tensile Stress	Yield,23°C	ISO527-2	75.0	Mpa
Tensile Strain	Yield,23°C	ISO527-2	4.0	%
Tensile Modulus	23°C	ISO527-2	3500	Mpa
Tensile Elongation	Yield,23°C	ASTMD638	5.0	%
Tensile Elongation	Tensile Elongation	Break,23°C	ASTMD638	50	%
Flexural Modulus	23°C	ASTMD790	3000	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	3000	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ASTMD648	224	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed	ASTMD648	91.0	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	70.0	°C
RTIElec	0.38mm	UL746	110	°C
	RTIElec	0.75mm	UL746	120	°C
		RTIElec	1.5mm	UL746	120	°C
		RTIElec	RTIElec	3.0mm	UL746	120	°C
Evolution Calendar intelligent importer	0.38mm	UL746	65.0	°C
	Evolution Calendar intelligent importer	0.75mm	UL746	105	°C
		Evolution Calendar intelligent importer	1.5mm	UL746	105	°C
		Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	105	°C
RTIStr	0.38mm	UL746	65.0	°C
	RTIStr	0.75mm	UL746	115	°C
		RTIStr	1.5mm	UL746	120	°C
		RTIStr	RTIStr	3.0mm	UL746	120	°C
Peak Melting Temperature		ASTMD3418	243	°C
Melting temperature (DSC)		ISO3146	243	°C
Linear thermal expansion coefficient	MD	ASTME831	4E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD		8E-05	cm/cm/°C
	Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD		9E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	32	KV/mm
Comparative Tracking Index		IEC60112	600	V
Volume Resistivity	1.50mm	ASTMD257	1E+13	ohms·cm
Dissipation Factor?	1MHz	IEC60250	0.020
Dielectric Constant	1MHz	IEC60250	3.60
Volume Resistivity		IEC60093	1E+13	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	23°C	ISO179	80	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179	4.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	9.0	kJ/m²
Notched Izod Impact Strength	-40°C	ASTMD256	32	J/m
	Notched Izod Impact Strength	23°C	ASTMD256	43	J/m
	Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180	4.5	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	100	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.38mm	UL94	V-0
	UL flame retardant rating	0.75mm	UL94	V-0
		UL flame retardant rating	1.5mm	UL94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	V-0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.