PEI ULTEM™ 1000-7101 SABIC INNOVATIVE SHANGHAI

Unit Price:
$23930 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	24 hr	ASTM D570	0.25	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C	ASTM D570	1.3	%
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	9.0	g/10 min
Modeling Shrinkage - Flow	3.20 mm	内部方法	0.50 到 0.70	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Yield	ASTM D638	7.0	%
Tensile Elongation	Tensile Elongation	Break	ASTM D638	60	%
Tensile Strength	Yield	ASTM D638	110	Mpa
Tensile Modulus		ASTM D638	3580	Mpa
Poisson Ratio		ASTM E132	0.36
Flexural Modulus	100 mm Span	ASTM D790	3510	Mpa
Flexural Strength	Yield, 100 mm Span	ASTM D790	165	Mpa
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Thermal Conductivity		ASTM C177	0.22	W/m/K
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Coefficient of Linear Thermal Expansion	Flow : -20 to 150°C	ASTM E831	5.6E-5	cm/cm/°C
Coefficient of Linear Thermal Expansion	Coefficient of Linear Thermal Expansion	Across Flow : -20 to 150°C	ASTM E831	5.4E-5	cm/cm/°C
Deflection Temperature Under Load	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	210	°C
Deflection Temperature Under Load	Deflection Temperature Under Load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	201	°C
Vicat Softening Temperature		ASTM D15254	218	°C

Electrical Properties	Test Condition	Test Method	Test Result	Unit
Arc Resistance		ASTM D495	PLC 5
High Amp Arc Ignition		UL 746	PLC 3
High Voltage Arc Tracking Rate		UL 746	PLC 2
Comparative Tracking Index		UL 746	PLC 4
Hot-wire Ignition		UL 746	PLC 1
Dielectric Strength	1.60 mm, in Air	ASTM D149	33	KV/mm
	Dielectric Strength	1.60 mm, in Oil	ASTM D149	28	KV/mm
	Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	ASTM D149	20	KV/mm
Dielectric Constant	100 Hz	ASTM D150	3.15
Dielectric Constant	Dielectric Constant	1 kHz	ASTM D150	3.15
Volume Resistivity		ASTM D257	1.0E+17	ohms·cm
Dissipation Factor	100 Hz	ASTM D150	1.5E-3
	Dissipation Factor	1 kHz	ASTM D150	1.2E-3
	Dissipation Factor	Dissipation Factor	2.45 GHz	ASTM D150	2.5E-3

Injection	Test Result	Unit
Drying Time	4.0 到 6.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	330 到 400	°C
Middle Temperature	340 到 400	°C
Front Temperature	345 到 400	°C
Nozzle Temperature	345 到 400	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	150	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	350 到 400	°C
Mold Temperature	135 到 165	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Gardner Impact	23°C	ASTM D3029	36.0	J
Unnotched Izod Impact Strength	23°C	ASTM D4812	1300	J/m
Reverse Notch Izod Impact	3.20 mm	ASTM D256	1300	J/m

Hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	M-Scale	ASTM D785	109

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ASTM D2863	47	%
Flame Rating	0.40 mm	UL 94	V-2
	Flame Rating	0.75 mm	UL 94	V-0
	Flame Rating	Flame Rating	3.0 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.