PEI ULTEM™ AUT200 BK1A113 SABIC INNOVATIVE SPAIN
39
- Unit Price:
- $11244 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 100MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 337°C/6.6kg | ASTMD1238 | 18 | g/10min |
| Melt Volume flow Rate | 360°C/5.0kg | ISO1133 | 25.0 | cm3/10min |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 1.3 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3520 | Mpa |
| Tensile Modulus | ASTMD638 | 3590 | Mpa | |
| Tensile Modulus | ISO527-2/1 | 3200 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 110 | Mpa |
| Tensile Stress | Yield | ISO527-2/5 | 105 | Mpa |
| Tensile Strength | Break | ASTMD638 | 105 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 85.0 | Mpa |
| Tensile Elongation | Yield | ASTMD638 | 7.0 | % |
| Tensile Strain | Yield | ISO527-2/5 | 6.0 | % |
| Tensile Elongation | Break | ASTMD638 | 60 | % |
| Tensile Strain | Break | ISO527-2/5 | 60 | % |
| Flexural Modulus | ISO178 | 3300 | Mpa | |
| Flexural Strength | ISO178 | 160 | Mpa | |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 165 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 205 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 197 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 199 | °C | |
| 1.8MPa,Unannealed,100mmSpan9 | ISO75-2/Ae | 190 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan10 | ISO75-2/Af | 193 | °C | |
| Vicat Softening Temperature | ASTMD152511 | 219 | °C | |
| -- | ISO306/B50 | 211 | °C | |
| -- | ISO306/B120 | 212 | °C | |
| Coefficient of Linear Thermal Expansion | MD：-40to150°C | ASTME831 | 5.5E-05 | cm/cm/°C |
| MD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-40to150°C | ASTME831 | 5.5E-05 | cm/cm/°C | |
| TD：23to150°C | ISO11359-2 | 5E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | NoBreak | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 33.0 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 3.0 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 5.0 | kJ/m² |
| 23°C | ISO180/1A | 5.0 | kJ/m² | |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak |
| Additional | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| MetallizedHazeOnset | 内部方法 | 204 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.