PEI ULTEM™ 2110EPR-7301 SABIC INNOVATIVE SHANGHAI

Unit Price:
$13870 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	337°C/6.6 kg	ASTM D1238	11	g/10 min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Break	ASTM D638	6.0	%
Flexural Modulus	100 mm Span	ASTM D790	5240	Mpa
Flexural Strength	Break, 100 mm Span	ASTM D790	199	Mpa
Tensile Modulus		ASTM D638	4610	Mpa
Tensile Strength	Yield	ASTM D638	114	Mpa
Tensile Strength	Tensile Strength	Break	ASTM D638	115	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	170	°C
RTI Imp		UL 746	170	°C
RTI Elec		UL 746	170	°C
Deflection Temperature Under Load	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	207	°C

Electrical Properties	Test Method	Test Result
Comparative Tracking Index	UL 746	PLC 4
Hot-wire Ignition	UL 746	PLC 1
High Amp Arc Ignition	UL 746	PLC 4
High Voltage Arc Tracking Rate	UL 746	PLC 2
Arc Resistance	ASTM D495	PLC 6

Injection	Test Result	Unit
Drying Time	4.0 到 6.0	hr
Suggested Shot Size	40 到 60	%
Rear Temperature	330 到 400	°C
Middle Temperature	340 到 400	°C
Front Temperature	345 到 400	°C
Nozzle Temperature	345 到 400	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	40 到 70	rpm
Vent Depth	0.025 到 0.076	mm
Drying Temperature	150	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	350 到 400	°C
Mold Temperature	135 到 165	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Reverse Notch Izod Impact	3.20 mm	ASTM D256	400	J/m

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.41 mm	UL 94	V-0
Flame Rating	Flame Rating	1.9 mm	UL 94	5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.