Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density / Specific Gravity | 23°C | ISO1183 | 1.30 | g/cm³ |
Melt Volume flow Rate | 380°C/5.0kg | ISO1133 | 12.0 | cm3/10min |
Modeling Shrinkage | TD:180°C,2.00mm | ISO294-4 | 1.1 | % |
Modeling Shrinkage | MD:180°C,2.00mm | ISO294-4 | 0.90 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2 | 3500 | Mpa |
Tensile Stress | Yield | ISO527-2 | 96.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 5.0 | % |
Tensile Strain | Break | ISO527-2 | 30 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | -- | ISO306/A | 335 | °C |
Vicat Softening Temperature | -- | ISO306/B | 305 | °C |
Melting Temperature | | ISO11357-3 | 340 | °C |
Coefficient of Linear Thermal Expansion | MD:23to55°C | ISO11359-2 | 6E-05 | cm/cm/°C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+14 | ohms |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Dielectric Strength | | IEC60243-1 | 16 | KV/mm |
Relative Permittivity | 50Hz | IEC60250 | 2.80 | |
Relative Permittivity | 1MHz | IEC60250 | 2.80 | |
Comparative Tracking Index | SolutionA5 | IEC60112 | 175 | V |
Comparative Tracking Index | SolutionA | IEC60112 | 200 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30°C,Complete Break | ISO179/1eA | 6.0 | kJ/m² |
Charpy Notched Impact Strength | 23°C,Complete Break | ISO179/1eA | 7.0 | kJ/m² |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 3.2mm | UL94 | V-0 | |
Glow Wire Flammability Index | 2.0mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 2.0mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.