Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 230°C/2.16kg | ISO1133 | 46.0 | cm3/10min |
Modeling Shrinkage | TD | ISO294-4 | 1.5 | % |
Modeling Shrinkage | MD | ISO294-4 | 1.3 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.70 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.30 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 5.0%Strain | ISO527-2 | 3.90 | Mpa |
Tensile Stress | 10%Strain | ISO527-2 | 6.60 | Mpa |
Tensile Stress | 50%Strain | ISO527-2 | 9.20 | Mpa |
Tensile Stress | 100%Strain | ISO527-2 | 9.30 | Mpa |
Nominal Tensile Strain at Break | | ISO527-2 | 800 | % |
Tensile Modulus | | ISO527-2 | 85.0 | Mpa |
Tensile Stress | Break | ISO527-2 | 23.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ISO306/B50 | 50.0 | °C |
Melting Temperature | | ISO11357-3 | 189 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 1.6E-04 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 1.6E-04 | cm/cm/°C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | IEC60093 | 1E+13 | ohms·cm |
Dielectric Strength | | IEC60243-1 | 20 | KV/mm |
Relative Permittivity | 1MHz | IEC60250 | 4.40 | |
Dissipation Factor | 1MHz | IEC60250 | 0.035 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D,3sec | ISO868 | 40 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.6mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.