Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | % | 0.50 | -- |
| Modeling Shrinkage | MD | % | 0.10 | -- |
| Moisture Absorption | Saturation,23°C | % | 0.80 | -- |
| Moisture Absorption | Equilibrium,23°C,50%RH | % | 0.40 | -- |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | MPa | 12000 | 11500 |
| Tensile Stress | Break | MPa | 155 | |
| Tensile Strain | Break | % | 5.0 | 6.0 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed | °C | 165 | -- |
| Heat Deflection Temperature | 8.0MPa,Unannealed | °C | 125 | -- |
| Continuous Use Temperature | --3 | °C | 90.0到120 | -- |
| Continuous Use Temperature | --4 | °C | 150 | -- |
| Melting Temperature | | °C | 178 | -- |
| Coefficient of Linear Thermal Expansion | MD | cm/cm/°C | 1.5E-05 | -- |
| Coefficient of Linear Thermal Expansion | TD | cm/cm/°C | 1.2E-04 | -- |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ohms | -- | 1E+12 |
| Volume Resistivity | | ohms·cm | -- | 1E+13 |
| Dielectric Strength | | kV/mm | -- | |
| Comparative Tracking Index | | V | -- | 600 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | kJ/m² | 90 | |
| Charpy Unnotched Impact Strength | 23°C | kJ/m² | 90 | |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D,15sec | | -- | 82 |
| Ball Indentation Hardness | | MPa | -- | 155 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.8mm | | HB | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.