PC Makrolon® 6485GR 901510 COVESTRO GERMANY
27
- Unit Price:
- $3159 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Modeling Shrinkage | TD | ISO2577 | 0.60to0.80 | % |
MD | ISO2577 | 0.60to0.80 | % | |
TD:2.00mm3 | ISO294-4 | 0.70 | % | |
MD:2.00mm3 | ISO294-4 | 0.65 | % | |
Moisture Absorption | Saturation,23°C | ISO62 | 0.30 | % |
Equilibrium,23°C,50%RH | ISO62 | 0.12 | % | |
Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
Density / Specific Gravity | 23°C | ISO1183 | 1.20 | g/cm³ |
Apparent Density | ISO60 | 0.64 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | >50 | % |
Flexural Strain | 23°C | ISO178 | 7.1 | % |
Flexural Stress | 3.5%Strain,23°C | ISO178 | 74.0 | Mpa |
23°C | ISO178 | 98.0 | Mpa | |
Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
Tensile Creep Modulus | 1hr | ISO899-1 | 2200 | Mpa |
Tensile Stress | Yield,23°C | ISO527-2/50 | 66.0 | Mpa |
Break,23°C | ISO527-2/50 | 65.0 | Mpa | |
Tensile Strain | Yield,23°C | ISO527-2/50 | 6.1 | % |
Break,23°C | ISO527-2/50 | 120 | % | |
Tensile Creep Modulus | 1000hr | ISO899-1 | 1900 | Mpa |
Tensile Modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 124 | °C |
0.45MPa,Unannealed | ISO75-2/B | 136 | °C | |
Ball PressureTest | 136°C | IEC60695-10-2 | Pass | |
RTIElec | 1.5mm | UL746 | 125 | °C |
RTIImp | 1.5mm | UL746 | 115 | °C |
RTIStr | 1.5mm | UL746 | 125 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 144 | °C |
-- | ISO306/B120 | 145 | °C | |
Coefficient of Linear Thermal Expansion | MD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C |
TD:23to55°C | ISO11359-2 | 6.5E-05 | cm/cm/°C | |
Glass Transition Temperature | ISO11357-2 | 142 | °C | |
Thermal Conductivity | 23°C | ISO8302 | 0.20 | W/m/K |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
Dissipation Factor | 23°C,100Hz | IEC60250 | 8E-04 | |
23°C,1MHz | IEC60250 | 9E-03 | ||
Relative Permittivity | 23°C,100Hz | IEC60250 | 3.10 | |
23°C,1MHz | IEC60250 | 3.00 | ||
Comparative Tracking Index | SolutionA | IEC60112 | 225 | V |
SolutionB | IEC60112 | 125 | V | |
Surface Resistivity | IEC60093 | 1E+16 | ohms | |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Unnotched Impact Strength | -60°C | ISO179/1eU | NoBreak | |
-30°C | ISO179/1eU | NoBreak | ||
23°C | ISO179/1eU | NoBreak | ||
Multi-Axial Instrumented Impact Energy | -30°C | ISO6603-2 | 55.0 | J |
23°C | ISO6603-2 | 50.0 | J | |
Charpy Notched Impact Strength | -30°C,Complete Break | ISO7391 | 14 | kJ/m² |
23°C,Partial Break | ISO7391 | 70 | kJ/m² | |
Notched Izod Impact Strength | -30°C,Complete Break | ISO7391 | 12 | kJ/m² |
23°C,Partial Break | ISO7391 | 65 | kJ/m² | |
Multi-Axial Instrumented Impact Peak Force | -30°C | ISO6603-2 | 6000 | N |
23°C | ISO6603-2 | 5200 | N |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Ball Indentation Hardness | ISO2039-1 | 115 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
FMVSS Flammability | >1.00mm | ISO3795 | passed | |
FlashIgnitionTemperature | ASTMD1929 | 460 | °C | |
Glow Wire Test | 1.50mm | EDFHN60E.02 | 750 | °C |
3.00mm | EDFHN60E.02 | 750 | °C | |
Needle Flame Test | MethodF:1.50mm | IEC60695-11-5 | 2.0 | min |
MethodF:2.00mm | IEC60695-11-5 | 2.0 | min | |
MethodF:3.00mm | IEC60695-11-5 | 2.0 | min | |
MethodK:1.50mm | IEC60695-11-5 | 2.0 | min | |
MethodK:2.00mm | IEC60695-11-5 | 2.0 | min | |
MethodK:3.00mm | IEC60695-11-5 | 2.0 | min | |
Oxygen Index | ISO4589-2 | 36 | % | |
SelfIgnitionTemperature | ASTMD1929 | 540 | °C | |
Flame Rating | 0.75mm | UL94 | V-1 | |
1.5mm | UL94 | V-0 | ||
3.0mm | UL94 | 5VA | ||
Glow Wire Flammability Index | 0.75mm | IEC60695-2-12 | 960 | °C |
1.5mm | IEC60695-2-12 | 960 | °C | |
3.0mm | IEC60695-2-12 | 960 | °C | |
ApplicationofFlamefromSmallBurner-MethodKandF | 2.00mm | DIN53438-1,-3 | K1,F1 | |
Glow Wire Ignition Temperature | 0.75mm | IEC60695-2-13 | 875 | °C |
1.5mm | IEC60695-2-13 | 875 | °C | |
3.0mm | IEC60695-2-13 | 875 | °C |
Additional | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
ElectrolyticalCorrosion | 23°C | IEC60426 | A1 | |
ISO Shortname | ISO7391-PC,MFR,(,,)-09-9 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.