Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 5.0 | g/10min |
Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 19 | g/10min |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.10to0.30 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.14 | % |
Moisture Absorption | Equilibrium,23°C | ASTMD570 | 0.26 | % |
Specific Volume | | ASTMD792 | 0.697 | cm³/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Break | ASTMD638 | 100 | Mpa |
Tensile Elongation | Break | ASTMD638 | 2.0 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 6610 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 153 | Mpa |
Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | ASTMD1044 | 24.0 | mg |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Specific Heat | | ASTMC351 | 1130 | J/kg/°C |
Thermal Conductivity | | ASTMC177 | 0.22 | W/m/K |
RTIElec | | UL746 | 120 | °C |
RTIImp | | UL746 | 120 | °C |
RTIStr | | UL746 | 130 | °C |
Heat Deflection Temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 151 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 146 | °C |
Vicat Softening Temperature | | ASTMD15255 | 165 | °C |
Coefficient of Linear Thermal Expansion | MD:-40to95°C | ASTME831 | 2.2E-05 | cm/cm/°C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Volume Resistivity | | ASTMD257 | >1.0E+17 | ohms·cm |
Dielectric Strength | 3.20mm,inAir | ASTMD149 | 19 | KV/mm |
Dielectric Constant | 50Hz | ASTMD150 | 3.35 | |
Dielectric Constant | 60Hz | ASTMD150 | 3.35 | |
Dielectric Constant | 1MHz | ASTMD150 | 3.31 | |
Dissipation Factor | 50Hz | ASTMD150 | 1.1E-03 | |
Dissipation Factor | 60Hz | ASTMD150 | 1.1E-03 | |
Dissipation Factor | 1MHz | ASTMD150 | 7E-03 | |
Arc Resistance | | ASTMD495 | PLC7 | |
Comparative Tracking Index | CTI | UL746 | PLC5 | |
High Amp Arc Ignition | HAI | UL746 | PLC4 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC3 | |
Hot-wire Ignition | HWI | UL746 | PLC0 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Gardner Impact | 23°C | ASTMD3029 | 5.00 | J |
Tensile Impact Strength | | ASTMD1822 | 67.0 | kJ/m² |
Hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | M-Sale | ASTMD785 | 92 | |
Rockwell Hardness | R-Sale | ASTMD785 | 120 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.75mm | UL94 | HB | |
Flame Rating | 1.5mm | UL94 | V-1 | |
Flame Rating | 3.0mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.