Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.44 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.12 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation (Break) | | ASTM D638/ISO 527 | 2.5 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 8240(84000) | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 121(1230) | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D790/ISO 178 | 7355(75100) | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 168(1700) | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ASTM D-790 | 7355(75100) | MPa(Kgf/cm |
Dielectric Constant | 10 | ASTM D-150 | 3.41 | |
Flexural Strength | | ASTM D-790 | 168(1700) | MPa(Kgf/cm |
Tensile Modulus | | ASTM D-638 | 8240(84000) | MPa(Kgf/cm |
Tensile Elongation | Break | ASTM D-638 | 2.5 | % |
Rockwell Hardness | | ASTM D-785 | 93 | M标度 |
Tensile Strength | | ASTM D-638 | 121(1230) | MPa(Kgf/cm |
Compressive Strength | | ASTM D-695 | 143(1460) | MPa(Kgf/cm |
Charpy Impact Strength | | ASTM D256/ISO 179 | 108(11) | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Temperature Index | 非冲击式,厚度1.47mm | UL 746B | 130 | °C |
Coefficient of Linear Thermal Expansion | Flow | ASTM D-696 | 2.0 | |
Coefficient of Linear Thermal Expansion | Across Flow | ASTM D-696 | 5.6 | |
Heat Deflection Temperature | 负荷1.813MPa(18.6kgf/cm | JIS K-7207 | 149 | °C |
Heat Deflection Temperature | 负荷0.451MPa(4.6kgf/cm | JIS K-7207 | 151 | °C |
Temperature Index | 电学式,厚度1.47mm | UL 746B | 130 | °C |
Temperature Index | 冲击式,厚度1.47mm | UL 746B | 120 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 艾氏、带Notched厚度6.4mm | ASTM D-256 | 108(11) | J/m(kgf·cm/cm) |
Dissipation Factor (Tangent) | 60Hz | ASTM D-150 | 0.0009 | |
Arc Resistance | | ASTM D-495 | 100 | sec |
Insulation Resistance | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm |
Volume Resistivity | | ASTM D-257 | 1×10 | Ω.cm |
Dielectric Constant | | ASTM D-150 | 3.51 | 60Hz |
Notched Izod Impact Strength | 艾氏、带Notched厚度3.2mm | ASTM D-256 | 108(11) | J/m(kgf·cm/cm) |
Dissipation Factor (Tangent) | 10 | ASTM D-150 | 0.009 | |
Comparative Tracking Index | | IEC 112 | 185 | V |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow | ASTM D-955 | 0.02~0.2 | % |
Modeling Shrinkage | Across Flow | ASTM D-955 | 0.3~0.5 | % |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr,in 23℃ | ASTM D-570 | 0.12 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.