Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1200 | |
Modeling Shrinkage | | ASTM D955 | 0.5-0.7 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.2 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 8.00 | cm3/10min |
Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 | % |
Modeling Shrinkage | MD:4.00mm | 内部方法 | 0.50to0.70 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1 | 2400 | Mpa |
Tensile Stress | Yield | ISO527-2/50 | 61.0 | Mpa |
Tensile Strain | Yield | ISO527-2/50 | 6.0 | % |
Nominal Tensile Strain at Break | | ISO527-2/50 | >50 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 61 | kg/cm²(MPa)[Lb/in²] |
Tensile Elongation | | ASTM D638/ISO 527 | 6 | % |
Flexural Modulus | | ASTM D790/ISO 178 | 2300 | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D790/ISO 178 | 91 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO178 | 2300 | Mpa |
Flexural Stress | | ISO178 | 91.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 142 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 129 | °C |
Vicat Softening Temperature | | ISO306/B50 | 149 | °C |
Coefficient of Linear Thermal Expansion | MD | ISO11359-2 | 7E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD | ISO11359-2 | 7E-05 | cm/cm/°C |
RTIElec | 1.5mm | UL746 | 125 | °C |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 149 | ℃(℉) |
Coefficient of Linear Thermal Expansion | | ASTM D696/ISO 11359 | 0.7 | mm/mm.℃ |
RTIImp | 1.5mm | UL746 | 115 | °C |
RTIStr | 1.5mm | UL746 | 125 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
Dielectric Strength | | IEC60243-1 | 30 | KV/mm |
Relative Permittivity | 100Hz | IEC60250 | 3.10 | |
Relative Permittivity | 1MHz | IEC60250 | 3.00 | |
Dissipation Factor | 100Hz | IEC60250 | 1E-03 | |
Dissipation Factor | 1MHz | IEC60250 | 9E-03 | |
Comparative Tracking Index | | IEC60112 | 250 | V |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.1 | |
Dielectric Constant | | ASTM D150/IEC 60250 | 3 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | | ISO179 | NoBreak | |
Optical | Test Condition | Test Method | Test Result | Unit |
---|
Transmittance | | ASTM D1003/ISO 13468 | 88 | % |
Index of Refraction | | ASTM D542/ISO 489 | 1.585 | |
Index of Refraction | | ASTMD542 | 1.585 | |
Light Transmittance | 3000µm | ASTMD1003 | 88.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.40mm | UL94 | V-2 | |
Flame Rating | 1.5mm | UL94 | V-2 | |
Flame Rating | 3.0mm | UL94 | V-2 | |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 875 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 850 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 875 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.