Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Viscosity Number | | ISO307 | 145 | cm³/g |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2/1A/1 | 5800 | Mpa |
| Tensile Stress | Break | ISO527-2/1A/5 | 120 | Mpa |
| Tensile Strain | Break | ISO527-2/1A/5 | 3.5 | % |
| Flexural Modulus | | ISO178 | 4300 | Mpa |
| Flexural Stress | | ISO178 | 170 | Mpa |
| Flexural Strain | | ISO178 | 6.5 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/Bf | 210 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/Af | 200 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 215 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 210 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 40 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 45 | kJ/m² |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 174 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Burning Rate | | ISO3795 | <100 | mm/min |
| Flame Rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| Flame Rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| Flame Rating | 3.0mm | IEC60695-11-10,-20 | HB | |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | -- | °C |
| Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | -- | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.