| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:280°C,2.00mm2 | ISO294-4 | 0.75 | % |
| Modeling Shrinkage | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.090 | % |
| Modeling Shrinkage | MD:280°C,2.00mm2 | ISO294-4 | 0.25 | % |
| Modeling Shrinkage | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.050 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23°C | ISO527-2/5 | 145 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2/5 | 3.5 | % |
| Tensile Modulus | 23°C | ISO527-2/1 | 9200 | Mpa |
| Flexural Stress | 23°C | ISO178 | 245 | Mpa |
| Flexural Modulus | 23°C | ISO178/A | 8500 | Mpa |
| Flexural Strain | 23°C | | 3.3 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed | ISO75-2/B | 210 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 200 | °C |
| Coefficient of Linear Thermal Expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | TD：23to55°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 220 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 60 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 65 | kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 55 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 75 | kJ/m² |
| Additional | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortname | | ISO1874 | PA6-HI,GR,14-100,GF30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.