| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | ISO 294-4 | 0.40-0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO 527-2 | 2050 | Mpa |
| Tensile Stress(Break) | | ISO 527-2 | 20.0 | Mpa |
| Tensile Strain(Break) | | ISO 527-2 | 55 | % |
| Tensile Creep Modulus | 1hr | ISO 899-1 | 2000 | Mpa |
| Flexural Modulus | | ISO 178 | 2000 | Mpa |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 9.00 | KJ/m |
| Notched Izod Impact Strength | | ISO 180/1A | 10.00 | KJ/m |
| Rockwell Hardness | | ISO 2039-2 | 76 | R scale |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.80MPa，Unannealed | ISO 75-2/A | 74.0 | °C |
| Heat Deflection Temperature | 1.80MPa，Annealed | ISO 75-2/A | 90.0 | °C |
| Heat Deflection Temperature | 1.80MPa | ISO 75-2 | 89.5 | °C |
| Vicat Softening Temperature | | ISO 306/A50 | 96.0 | °C |
| Vicat Softening Temperature | | ISO 306/B50 | 88.0 | °C |
| Vicat Softening Temperature | 50℃/h,B(50N) | ISO 306 | 88.0 | °C |
| Coefficient of Linear Thermal Expansion | Transverse | ISO 11359-2 | 0.000090 | cm/cm/℃ |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 | ohms |
| Dielectric Strength | | IEC 60243-1 | 150.00 | KV/mm |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ISO 1183 | 1.04 | g/cm |
| Melt Mass-Flow Rate | 200℃,5kg | ISO 1133 | 10 | g/10min |
| Moisture Absorption | 24hr,23℃ | ISO 62 | 0.10 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.