Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 10.5 | % |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | | 0.4-0.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Strength | | ISO 178 | 32 | Mpa |
| Notched Izod Impact Strength | 23℃ | ISO 180 | 10 | kJ/m² |
| Rockwell Hardness | | ASTM D-785 | 70 | L标尺 |
| Rockwell Hardness | | ASTM D785 | 70 | |
| Flexural Strength | | ASTM D790/ISO 178 | 32 | kg/cm²(MPa)[Lb/in²] |
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 11 | kJ/m² |
| Tensile Stress(Yield) | | ISO 527 | 21 | Mpa |
| Tensile Elongation (Break) | | ISO 527 | 40 | % |
| Tensile Elongation (Break) | | ASTM D638/ISO 527 | 40 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTM D1525/ISO R306 | 90 | ℃（℉） |
| Heat Deflection Temperature | | ISO 75 | 88 | °C |
| Flame Rating | | UL 94 | HB | |
| Vicat Softening Temperature | | ISO 306 | 90 | °C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC6093 | >1014 | Ω.cm |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 180-260 | °C |
| Melt Temperature | | | 180-240 | °C |
| Melt Temperature | | | 10-60 | °C |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | | ISO 62 | <0.1 | % |
| Density | | ISO 1183 | 1.05 | g/cm³ |
| Melt Mass-Flow Rate | | ISO 1133 | 3.2 | cm3/10min |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO 527 | 1600 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.