Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ASTMD792 | 1.29 | g/cm³ |
| Melt Mass-Flow Rate | 365°C/5.0kg | ASTMD1238 | 14to20 | g/10min |
| Modeling Shrinkage | MD：3.18mm | ASTMD955 | 0.70 | % |
| Moisture Absorption | 24hr | ASTMD570 | 0.37 | % |
| Moisture Absorption | Equilibrium | ASTMD570 | 1.1 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 3.18mm | ASTMD638 | 2340 | Mpa |
| Tensile Strength | 3.18mm | ASTMD638 | 69.6 | Mpa |
| Tensile Elongation | Yield,3.18mm | ASTMD638 | 7.2 | % |
| Tensile Elongation | Break,3.18mm | ASTMD638 | 60to120 | % |
| Flexural Modulus | 3.17mm | ASTMD790 | 2410 | Mpa |
| Flexural Strength | 5.0%Strain,3.18mm | ASTMD790 | 91.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.18mm | ASTMD648 | 207 | °C |
| Glass Transition Temperature | | ASTME1356 | 220 | °C |
| Linear thermal expansion coefficient | MD：3.18mm | ASTMD696 | 5.6E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | ASTMD257 | 9E+15 | ohms·cm |
| Dielectric Strength | 0.0254mm | ASTMD149 | >200 | KV/mm |
| Dielectric Strength | 3.18mm | ASTMD149 | 15 | KV/mm |
| Dielectric Constant | 3.18mm,60Hz | ASTMD150 | 3.44 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 3.17mm | ASTMD256 | 690 | J/m |
| TensileImpactStrength | 3.18mm | ASTMD1822 | 399 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index of light | | ASTMD542 | 1.672 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 0.76mm | UL94 | V-0 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| SteamSterilization-w/Morpholine5 | | | >1000 | cycles |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.