optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.490
transmissivity		ASTM D1003	92.0	%
turbidity		ASTM D1003	0.50	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/2U	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	Yield, 23°C	ISO 527-2	70.0	Mpa
Tensile strain	Break, 23°C	ISO 527-2	6.0	%
Bending modulus	23°C	ISO 178	3300	Mpa
bending strength	23°C	ISO 178	103	Mpa
Compressive stress	23°C	ISO 604	117	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			85 to 90	°C
drying time			2.0 to 4.0	hr
Processing (melt) temperature			230 to 250	°C
Mold temperature			80 to 90	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	103	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	100	°C
Vicat softening temperature		ISO 306/B	108	°C
Linear coefficient of thermal expansion	-30 to 23°C，Flow	ASTM D696	6.5E-5	cm/cm/°C
specific heat			2090	J/kg/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	230°C/3.8 kg	ISO 1133	2.8	g/10 min
Shrinkage rate	Flow	ASTM D955	0.20 - 0.60	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		ASTM D257	> 1.0E+14	ohms
Volume resistivity		ASTM D257	> 1.0E+15	ohms·cm
Dielectric strength		ASTM D149	20	KV/mm
Dielectric constant	60 Hz	ASTM D150	3.70
Dissipation factor	1 MHz	ASTM D150	0.040
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ASTM D785	97

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.