Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ASTM D638	4610 Mpa
tensile strength		ASTM D638	114 Mpa
tensile strength	tensile strength		ASTM D638	115 Mpa
elongation		ASTM D638	6.0 %
Flexural modulus		ASTM D790	5240 Mpa
bending strength		ASTM D790	199 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Reverse notch impact		ASTM D256	400 J/m

Electrical performance	Test Method	Test Result
arc resistance	ASTM D495	PLC 6
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 4
High arc combustion index (HAI)	UL 746	PLC 4
High Voltage Arc Traceability Rate (HVTR)	UL 746	PLC 2
Hot wire ignition (HWI)	UL 746	PLC 1

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			330 to 400 °C
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
Temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

Thermal performance	Test Method	Test Result
Heat distortion temperature	ASTM D648	207 °C
RTI Elec	UL 746	170 °C
RTI Imp	UL 746	170 °C
RTI	UL 746	170 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.