TPEE LONGLITE® 1163LL TAIWAN CHANGCHUN
225
- Unit Price:US$ 3,228 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:47.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Creep resistance｜antioxidant｜Fatigue resistance
- Application Areas:Cable｜Fitness equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 30 g/10 min | |
| Shrinkage rate | ISO 294-4 | 1.3 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.5 % | ||
| Shrinkage rate | ISO 294-4 | 1.7 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 63 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shore hardness | ISO 868 | 63 | |
| Tensile modulus | 511 Mpa | ||
| tensile strength | ISO 527-2 | 33.0 Mpa | |
| Tensile strain | ISO 527-2 | 490 % | |
| Flexural modulus | ISO 178 | 183 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 无断裂 | |
| tensile strength | ISO 527 | 36 Mpa | |
| elongation at break | ISO 527 | 460 % | |
| Flexural elasticity | ISO 178 | 300 Mpa | |
| Impact strength of cantilever beam gap | ISO 179/IeA | PARTIAL BREAK kJ/㎡ | |
| Volume resistivity | IEC 60093 | 7.0E 13 Ohm cm | |
| IEC 60093 | 3.0E 13 Ohm | ||
| dielectric strength | IEC 60243 | 17 KV/mm |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ISO 527 | 36 Mpa |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 2.8E+15 Ohm | |
| Volume resistivity | IEC 60093 | 6.3E+13 ohm·cm | |
| dielectric strength | IEC 60243-1 | 17 KV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 212 °C | |
| ISO 3146C | 211 °C | ||
| melt mass-flow rate | ISO 1133 | 8 g/10 min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.